Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 0.9-0.91 | |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃/2.16 kg | ISO 1133 | 1.5 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ASTM D638/ISO 527 | 106000psi | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | ASTM D790/ISO 178 | 94300psi | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | 23°C, Injection | ISO 178 | 650 | Mpa |
| Coefficient of Friction | 与自身 - 动态 | ASTM D1894 | >0.25 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting Temperature | DSC | ISO 3146 | 133-136 | °C |
| Vicat Softening Temperature | | ISO 306/A50 | 115 | °C |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 239 | ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 50.0 µm | ASTM D1003 | < 3.0 | % |
| Gloss | 20°, 50.0 µm | ASTM D2457 | > 85 | |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | MD | ISO 527-3 | 30.0-40.0 | Mpa |
| Tensile Strength | TD | ISO 527-3 | 25.0-35.0 | Mpa |
| Tensile Modulus (MD) | 50 µm | ISO 527-3 | 730 | Mpa |
| Gardner Impact | 50 µm | ISO 7765-1 | 50 | g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.