Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:2.00mm | 内部方法 | 1.1 | % |
| Modeling Shrinkage | MD:2.00mm | 内部方法 | 0.20 | % |
| Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 2.0 | g/10min |
| Density | | ISO1183 | 1.12 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | 注塑 | ISO178 | 135 | Mpa |
| Tensile Stress | 屈服,注塑 | ISO527-2 | 100 | Mpa |
| Tensile Strain | 屈服,注塑 | ISO527-2/50 | 3.3 | % |
| Tensile Modulus | 注塑 | ISO527-2/1 | 6900 | Mpa |
| Flexural Modulus | 注塑 | ISO178 | 6000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 159 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 143 | °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 164 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 135 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -20°C,注塑 | ISO179/1eU | 49 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C,注塑 | ISO179/1eU | 58 | kJ/m² |
| Charpy Notched Impact Strength | 23°C,注塑 | ISO179/1eA | 12 | kJ/m² |
| Charpy Notched Impact Strength | -20°C,注塑 | ISO179/1eA | 9.0 | kJ/m² |
| Notched Izod Impact Strength | -20°C,注塑 | ISO180/1A | 8.5 | kJ/m² |
| Notched Izod Impact Strength | 23°C,注塑 | ISO180/1A | 11 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 112 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.