Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 0.9 | |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 7 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | 内部方法 | 1.4 | % |
| Modeling Shrinkage | MD | 内部方法 | 1.4 | % |
| Melt Mass-Flow Rate | | ASTMD1238 | 7.0 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength(Break) | | ASTM D-638 | 27.5 | Mpa |
| Tensile Strength | Break | ASTMD638 | 45.0 | Mpa |
| Tensile Elongation | Break | ASTM D-638 | >880 | % |
| Tensile Elongation | Yield | ASTMD638 | >800 | % |
| Rockwell Hardness | | ASTM D785 | 89 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 1030 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | ASTMD790 | 1030 | Mpa |
| Izod notch impact strength | | ASTM D256/ISO 179 | 3.6 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | | 151 | °C |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 108 | ℃（℉） |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 108 | °C |
| Melting Temperature | | | 150 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 89 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D-792 | 0.90 | g/cm |
| Melt index | | ASTM D-1238 | 7 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.