Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | 内部方法 | 1.5 | % |
Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 21 | g/10min |
Apparent Density | | ASTMD1895 | 0.50to0.60 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO527-2/50 | 34.0 | Mpa |
Tensile Strain | Yield | ISO527-2/50 | 8.0 | % |
Tensile Modulus | | ISO527-2/1 | 1500 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 94.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 53.0 | °C |
Vicat Softening Temperature | -- | ISO306/A50 | 153 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 90.0 | °C |
RTIElec | 2.0mm | UL746 | 120 | °C |
Evolution Calendar intelligent importer | 2.0mm | UL746 | 120 | °C |
RTIStr | 2.0mm | UL746 | 120 | °C |
BallIndentationTemperature2 | | IEC60695-10-2 | 125 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -20°C | ISO179/1eU | 15 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 80 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ISO2039-2 | 102 | |
Ball Indentation Hardness | H358/30 | ISO2039-1 | 70.0 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Gloss | 20°,2.00µm | DIN67530 | 70 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 2.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.