Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 45 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 230°C/2.16kg | ASTMD1238 | 45 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | -20℃ | ASTM D-256 | 4.0 | kg.cm/cm |
Notched Izod Impact Strength | 23℃ | ASTM D-256 | 7.0 | kg.cm/cm |
Notched Izod Impact Strength | 0℃ | ASTM D-256 | 4.5 | kg.cm/cm |
Tensile Strength | | ASTM D-638 | 290 | kg/cm |
Tensile Strength | Yield | ASTMD638 | 27.5 | Mpa |
Bending elasticity | | ASTM D-790 | 15000 | kg/cm |
Tensile Elongation | | ASTM D-638 | 200 | % |
Rockwell Hardness | | ASTM D-785 | 90 | R-Scale |
Flexural Modulus | | ASTMD790 | 1470 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 15000 | kg/cm²(MPa)[Lb/in²] |
Charpy impact strength | | ASTM D256/ISO 179 | 7.0 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 120 | °C |
Vicat Softening Temperature | | ASTM D-1525 | 150 | °C |
Deflection Temperature Under Load? | | ASTM D-648 | 120 | °C |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 85 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | HB | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | | ASTM D-1238 | 45 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.