Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.08	kg·cm/cm(J/M)ft·lb/in
Melt Mass-Flow Rate		ASTM D1238/ISO 1133	9	g/10min

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	220°C/10.0kg	ISO1133	9.0	g/10min
Melt Volume flow Rate	220°C/10.0kg	ISO1133	9.54	cm3/10min
Modeling Shrinkage	MD	ASTMD955	0.40到0.60	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Yield	ISO527-2/5	73.7	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	2	%
Tensile Strength		ASTM D638/ISO 527	76	kg/cm²(MPa)[Lb/in²]
Flexural Modulus		ASTM D790/ISO 178	3528	kg/cm²(MPa)[Lb/in²]
Flexural Strength		ASTM D790/ISO 178	108	kg/cm²(MPa)[Lb/in²]
Flexural Modulus		ISO178	3750	Mpa
Flexural Stress		ISO178	139	Mpa
Izod notch impact strength		ASTM D256/ISO 179	18	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ISO306/B	105	°C
RTI		UL746	50.0	°C
Ball PressureTest		EMAC	95	°C
Deflection Temperature Under Load?		ASTM D648/ISO 75	94	℃（℉）
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	89.3	°C
Vicat Softening Temperature		ASTM D1525/ISO R306	112	℃（℉）
RTIElec		UL746	50.0	°C
Evolution Calendar intelligent importer		UL746	50.0	°C

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.