ABS CYCOLAC™ FR23-NA1000 SABIC INNOVATIVE US
96
- Unit Price:
- $3851 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 44.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility flexibility Flame retardant
- Application Areas:Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 230°C/3.8 kg | ASTM D1238 | 6.8 | g/10 min |
| 220°C/5.0 kg | ISO 1133 | 9.0 | g/10 min | |
| Melt Volume flow Rate | 220°C/10.0 kg | ISO 1133 | 37.0 | cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ASTM D638 | 2410 | Mpa | |
| Tensile Elongation | Yield | ASTM D638 | 2.1 | % |
| Break | ASTM D638 | 11 | % | |
| Tensile Strength | Yield | ASTM D638 | 42.0 | Mpa |
| Break | ASTM D638 | 35.0 | Mpa | |
| Flexural Modulus | 50.0 mm Span | ASTM D790 | 2720 | Mpa |
| Flexural Strength | Yield, 50.0 mm Span | ASTM D790 | 73.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 83.0 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 72.0 | °C | |
| Vicat Softening Temperature | ASTM D15255 | 90.0 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C | |
| RTI | UL 746 | 60.0 | °C | |
| RTI Imp | UL 746 | 60.0 | °C | |
| RTI Elec | UL 746 | 60.0 | °C |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 200°C, 1000 sec^-1 | ASTM D3835 | 310 | Pa·s |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 80 到 90 | °C | ||
| Suggested Max Moisture | 0.10 | % | ||
| Processing (Melt) Temp | 200 到 220 | °C | ||
| Mold Temperature | 50 到 70 | °C | ||
| Drying Time | 2.0 到 4.0 | hr | ||
| Suggested Shot Size | 50 到 70 | % | ||
| Rear Temperature | 170 到 180 | °C | ||
| Middle Temperature | 195 到 205 | °C | ||
| Front Temperature | 200 到 215 | °C | ||
| Nozzle Temperature | 200 到 220 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 30 到 60 | rpm | ||
| Vent Depth | 0.038 到 0.051 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 41.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 2.3 mm | UL 94 | V-0 | |
| 2.5 mm | UL 94 | 5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.