ABS LNP™ STAT-KON™ A3000 BK8115 SABIC INNOVATIVE US
38
- Unit Price:
- $3241 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 24hr | ASTM D955 | 0.40 | % |
| Across Flow : 24hr | ASTM D955 | 0.50 | % | |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 1.1 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Yield 3 | ASTM D638 | 39.0 | Mpa |
| Yield | ISO 527-2/5 | 38.0 | Mpa | |
| Break 3 | ASTM D638 | 36.0 | Mpa | |
| Break | ISO 527-2/5 | 31.0 | Mpa | |
| Tensile Modulus | -- 2 | ASTM D638 | 2060 | Mpa |
| -- | ISO 527-2/1 | 2010 | Mpa | |
| Tensile Elongation | Yield 3 | ASTM D638 | 3.1 | % |
| Yield | ISO 527-2/5 | 3.0 | % | |
| Break 3 | ASTM D638 | 6.0 | % | |
| Break | ISO 527-2/5 | 24 | % | |
| Flexural Modulus | 50.0 mm Span 4 | ASTM D790 | 2090 | Mpa |
| -- 5 | ISO 178 | 1980 | Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 59.0 | Mpa |
| Break, 50.0 mm Span 4 | ASTM D790 | 65.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 88.0 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 7 | ISO 75-2/Bf | 91.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 76.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 7 | ISO 75-2/Af | 76.0 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831 | 9.3E-5 | cm/cm/°C |
| Flow : 23 to 60°C | ISO 11359-2 | 9.3E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 1.0E-4 | cm/cm/°C | |
| Across Flow : 23 to 60°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+9 到 1.0E+11 | ohms |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 4.0 | hr | ||
| Rear Temperature | 180 到 195 | °C | ||
| Middle Temperature | 195 到 205 | °C | ||
| Front Temperature | 205 到 215 | °C | ||
| Back Pressure | 0.200 到 0.300 | Mpa | ||
| Screw Speed | 30 到 60 | rpm | ||
| Drying Temperature | 70 到 80 | °C | ||
| Suggested Max Moisture | 0.050 到 0.10 | % | ||
| Processing (Melt) Temp | 200 到 210 | °C | ||
| Mold Temperature | 10 到 50 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812, ISO 180/1U | 无断裂 | |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 32.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.