Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 35 | g/10min |
Modeling Shrinkage | MD | ASTMD955 | 0.40to0.70 | % |
Density / Specific Gravity | | ASTMD792 | 1.16 | g/cm³ |
Density / Specific Gravity | | ISO1183 | 1.17 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO527-2/50 | 46.0 | Mpa |
Tensile Strain | Break | ISO527-2/50 | >5.0 | % |
Tensile Modulus | | ISO527-2/1 | 2600 | Mpa |
Flexural Modulus | | ASTMD790 | 2230 | Mpa |
Tensile Strength | Yield | ASTMD638 | 41.0 | Mpa |
Tensile Elongation | Break | ASTMD638 | >5.0 | % |
Flexural Strength | | ASTMD790 | 66.0 | Mpa |
Flexural Stress | | ISO178 | 68.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 82.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 76.0 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 12 | kJ/m² |
Notched Izod Impact Strength | 23°C,3.20mm | ASTMD256 | 190 | J/m |
Notched Izod Impact Strength | 23°C,12.7mm | ASTMD256 | 140 | J/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 105 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
UL flame retardant rating | 2.0mm | UL94 | 5VB | |
UL flame retardant rating | 2.5mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.