ABS TAITALAC® 1000T TAIDA TAIWAN
90
- Unit Price:
- $1629 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High gloss High mobility Fatigue resistance Moderate impact resistanc
- Application Areas:battery Electrical enclosure Electrical appliances TV casing furniture Toy Footwear
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 200℃/5.0 kg | ASTM D1238 | 1.8 | g/10 min |
| 220℃/10.0 kg | ASTM D1238 | 18 | g/10 min | |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 1.8 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 18 | g/10min | |
| Moisture Absorption | Saturation | ASTM D570 | < 0.30 | % |
| Saturation | ASTMD570 | <0.30 | % | |
| Modeling Shrinkage | MD | ASTM D955 | < 0.40 | % |
| MD | ASTMD955 | <0.40 | % | |
| Density / Specific Gravity | ASTMD792 | 1.03 | g/cm³ | |
| ASTM D792 | 1.03 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | Yield,23°C | ASTMD790 | 68.9 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 2340 | Mpa |
| Tensile Strength | Yield,23°C,3.18mm | ASTMD638 | 40.0 | Mpa |
| Tensile Elongation | Break,23°C,3.18mm | ASTMD638 | 30 | % |
| Tensile Strength | Break,23°C,3.18mm | ASTMD638 | 35.2 | Mpa |
| Tensile Elongation | Break, 23℃, 3.18 mm | ASTM D638 | 30 | % |
| Rockwell Hardness | R-Scale, 23℃ | ASTM D785 | 110 | |
| Flexural Modulus | 23℃ | ASTM D790 | 2340 | Mpa |
| Flexural Strength | Yield, 23℃ | ASTM D790 | 68.9 | Mpa |
| Tensile Strength | Yield, 23℃, 3.18 mm | ASTM D638 | 40 | Mpa |
| Break, 23℃, 3.18 mm | ASTM D638 | 35.2 | Mpa | |
| Notched Izod Impact Strength | 23℃, 3.18 mm | ASTM D256 | 260 | J/m |
| 23℃, 6.35 mm | ASTM D256 | 230 | J/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTM D1525 | 103 | °C | |
| Deflection Temperature Under Load? | 1.8 MPa, Annealed, 12.7 mm | ASTM D648 | 86 | °C |
| 1.8MPa,Annealed,12.7mm | ASTMD648 | 86.0 | °C | |
| Flame Rating | 1.59 mm | UL 94 | HB | |
| RTIElec | 1.6mm | UL746 | 60.0 | °C |
| Evolution Calendar intelligent importer | 1.6mm | UL746 | 60.0 | °C |
| RTIStr | 1.6mm | UL746 | 60.0 | °C |
| High Amp Arc Ignition | 1.57 mm | UL 746 | 200 | |
| High Voltage Arc Tracking Rate | 1.57 mm | UL 746 | 0.00 | mm/min |
| Hot-wire Ignition | 1.57 mm | UL 746 | 17 | sec |
| Vicat Softening Temperature | ASTMD15255 | 103 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High Amp Arc Ignition | 1.57mm | UL746 | 200 | |
| High Amp Arc Ignition | 1.57mm | UL746 | 0.00 | mm/min |
| Hot-wireIgnition | 1.57mm | UL746 | 17 | sec |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 260 | J/m |
| 23°C,6.35mm | ASTMD256 | 230 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Sale,23°C | ASTMD785 | 110 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.6mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.