Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 0.40to0.70 | % |
Modeling Shrinkage | | ISO294-4 | 0.40to0.70 | % |
Moisture Absorption | Saturation,23°C | ASTMD570 | 1.0 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 1.0 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.22 | % |
Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 1.5 | g/10min |
Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 19 | g/10min |
Melt Volume flow Rate | 230°C/3.8kg | ASTMD1238 | 4.80 | cm3/10min |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 19.0 | cm3/10min |
Density / Specific Gravity | | ASTMD792 | 1.04 | g/cm³ |
Density / Specific Gravity | | ISO1183 | 1.04 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | 23°C | ISO527-2 | 10 | % |
Flexural Stress | | ISO178 | 65.0 | Mpa |
Tensile Strength | Yield,23°C | ASTMD638 | 45.0 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 45.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 2.6 | % |
Tensile Modulus | | ASTMD638 | 2300 | Mpa |
Tensile Modulus | | ISO527-2 | 2300 | Mpa |
Tensile Elongation | Break | ASTMD638 | 2.6 | % |
Flexural Modulus | | ASTMD790 | 2300 | Mpa |
Flexural Strength | | ASTMD790 | 65.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 90.6 | °C |
Deflection Temperature Under Load? | 0.45MPa,Annealed | ASTMD648 | 104 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 77.8 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed | ASTMD648 | 98.9 | °C |
Vicat Softening Temperature | -- | ISO306/A50 | 105 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 96.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 8.0E-5to1.1E-4 | cm/cm/°C |
Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 99.0 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 94.0 | °C |
Thermal Conductivity | | DIN52612 | 0.17 | W/m/K |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 100Hz | IEC60250 | 4.8E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 7.9E-03 | |
Relative Permittivity | 100Hz | IEC60250 | 2.90 | |
Relative Permittivity | 1MHz | IEC60250 | 2.80 | |
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Dielectric Constant | 1.00mm,1MHz | ASTMD150 | 2.80 | |
Volume Resistivity | | ASTMD257 | >1.0E+15 | ohms·cm |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 100 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 180 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179 | 8.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179 | 22 | kJ/m² |
Notched Izod Impact Strength | -30°C | ASTMD256 | 59 | J/m |
Notched Izod Impact Strength | -18°C | ASTMD256 | 100 | J/m |
Notched Izod Impact Strength | 23°C | ASTMD256 | 300 | J/m |
Notched Izod Impact Strength | -30°C | ISO180/A | 8.0 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/A | 26 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 103 | |
Ball Indentation Hardness | | ISO2039-1 | 97.0 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
The Yellow Index | | DIN6167 | 13 | YI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.