ABS POLYLAC® PA-705 TAIWAN CHIMEI

Unit Price:
$1768 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate		ASTM D1238/ISO 1133	2.7	g/10min
Melt Mass-Flow Rate	Melt Mass-Flow Rate		ASTM D1238/ISO 1133	27	g/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Bending elasticity	2.8mm/min	ASTM D-790	24000	kg/cm
Tensile Elongation	6mm/min	ASTM D-638	20	%
Tensile strength	6mm/min	ASTM D-638	450	kg/cm
Tensile Strength		ASTM D638/ISO 527	450	kg/cm²(MPa)[Lb/in²]
Tensile Elongation		ASTM D638/ISO 527	20	%
Rockwell Hardness		ASTM D785	110
Rockwell Hardness	Rockwell Hardness		ASTM D-785	110	R scale
Flexural Modulus		ASTM D790/ISO 178	24000	kg/cm²(MPa)[Lb/in²]
Flexural Strength		ASTM D790/ISO 178	680	kg/cm²(MPa)[Lb/in²]
Flexural Strength	Flexural Strength	2.8mm/min	ASTM D-790	680	kg/cm
Izod Impact Strength	1/4"	ASTM D-256	16	kg-cm/cm
Izod notch impact strength		ASTM D256/ISO 179	16	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	1kg*50℃/hr	ASTM D-792	104	°C
Vicat Softening Temperature		ASTM D1525/ISO R306	104	℃（℉）

Physical	Test Condition	Test Method	Test Result	Unit
Melt index	200℃*5kg	ASTM D-1238	2.7	g/10min
Melt index	Melt index	220℃*10kg	ASTM D-1238	27	g/10min

Other performance	Test Condition	Test Method	Test Result	Unit
Yellow index		ASTM D-1925	8.5(±)1.25

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.