ABS TAIRILAC® AG12A1 FORMOSA NINGBO
88
- Unit Price:
- $1564 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance wear resistant
- Application Areas:Household goods Plastic toy
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density / Specific Gravity | 23℃ | ASTM D-792 | 1.04 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact Strength | 23℃ | ASTM D-256 | 30 | kg-cm/cm |
| 1/4"厚 | ISO-R180 | 294 | J/m | |
| Tensile Strength | 23℃ | ASTM D-638 | 450 | kg/cm2 |
| 23℃ | ISO-527 | 44 | Mpa | |
| Flexural Strength | 23℃ | ASTM D-790 | 750 | kg/cm2 |
| 23℃ | ISO-178 | 74 | Mpa | |
| flexural modulus | 23℃ | ASTM D-790 | 25000 | kg/cm2 |
| 23℃ | ISO-178 | 2450 | Mpa | |
| Rockwell Hardness | 23℃ | ASTM D-785 | 105 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 18.6kg/cm2 | ASTM D-648 | 88 | °C |
| Flammability | E162823 | UL-94 | 1/16"HB |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 200℃ | ASTM D-1238 | 1.5 | g/10min |
| 220℃ | ISO-1133 | 15 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.