Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD	ASTMD955	0.40to0.70	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.40to0.70	%
Melt Mass-Flow Rate	220°C/10.0kg	ASTMD1238	28	g/10min
	Melt Mass-Flow Rate	230°C/3.8kg	ASTMD1238	8.0	g/10min
	Melt Mass-Flow Rate	Melt Mass-Flow Rate	220°C/10.0kg	ISO1133	28	g/10min
Apparent Density		ISO60	0.65	g/cm³
Melt Mass-Flow Rate	220°C/10.0kg	ASTMD1505	27.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominalstrainatbreak		ISO527-22	20	%
Flexural Modulus	3.20mm,InjectionMolded	ISO178	2400	Mpa
Tensile Strength	Break	ASTMD638	35.0	Mpa
Tensile Strength	Tensile Strength	Yield	ASTMD638	48.0	Mpa
Flexural Modulus		ASTMD790	2480	Mpa
Flexural Strength		ASTMD790	75.0	Mpa
Tensile Elongation	Break	ASTMD638	8.7	%
Flexural Strength	3.20mm,InjectionMolded	ISO178	70.0	Mpa
Tensile Elongation	Yield	ASTMD638	2.7	%
Tensile Stress	Yield,3.20mm,Injection	ISO527-2/50	45.0	Mpa
	Tensile Stress	Yield,3.20mm,Injection	ISO527-2/100	47.0	Mpa
	Tensile Stress	Tensile Stress	Yield	ISO527-22	48.0	Mpa
Tensile Strain	Yield,3.20mm,Injection	ISO527-2/50	2.5	%
Tensile Strain	Tensile Strain	Yield,3.20mm,Injection	ISO527-2/100	2.6	%
Tensile Modulus	3.20mm,Injection	ISO527-2	2340	Mpa
Tensile Modulus	Tensile Modulus		ISO527-22	2400	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	87.0	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	74.0	°C
		Deflection Temperature Under Load?	1.8MPa,Annealed	ISO75-2/A	95.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa	ISO75-22	95.0	°C
Vicat Softening Temperature		ASTMD15257	99.0	°C
	Vicat Softening Temperature		ISO306/B50	95.0	°C
	Vicat Softening Temperature	Vicat Softening Temperature	50N	ISO3062	92.0	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
CharpyNotchedImpactStrength	23°C	ISO179/1eA2	18.0	kJ/m²
Charpy impact strength	23°C	ISO179/1eU2	NoBreak
Charpy Notched Impact Strength	-30°C	ISO179/1eU2	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTMD785	108

Flammability	Test Condition	Test Method	Test Result	Unit
Burning Rate	2.00mm	ISO3795	60	mm/min
Flame Rating	1.5mm	UL94	HB
Flame Rating	Flame Rating	3.0mm	UL94	HB
Flame Rating (1.60 mm)	1.50mm,UL	4.21	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.