ABS STAREX® AS-0150 Samsung Cheil South Korea
85
- Unit Price:
- $2746 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity
- Application Areas:Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | ASTM-D955 | 0.3-0.6 | % | |
| Density / Specific Gravity | ASTM-D792 | 1.04 | g/cm |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | ASTM-D638 | 46 | Mpa | |
| Rockwell Hardness | ASTM-D785 | 104 | R-Scale | |
| Flexural Modulus | ASTM-D790 | 2273 | Mpa | |
| Flexural Strength | ASTM-D790 | 68 | Mpa | |
| IZOD Notch Impact Strength | 0.125in | ASTM-D256 | 6.1 | ft-1b/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 264psi Unannealed,0.250in | ASTM-D648 | 82.7 | °C |
| Vicat Softening Temperature | ISO R 306 | 97.7 | °C | |
| Flame Rating | 0.0591 in | UL94 | HB |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | ASTM-D570 | 0.3 | % | |
| Melt index | 220℃/10kg | ASTM-D1238 | 2.4 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.