Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.05 | |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 0.549 | g/10min |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow,23℃ | ISO 294-4 | 0.50-0.70 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress (Yield) | 23℃ | ISO 527-2 | 46.0 | Mpa |
Charpy Notched Impact Strength | -30℃ | ISO 179 | 10.00 | kJ/m² |
Charpy Notched Impact Strength | 23℃ | ISO 179 | 22.0 | kJ/m² |
Tensile Modulus | 23℃ | ISO 527-2 | 2150 | Mpa |
Rockwell Hardness | 23℃ | ISO 2039-2 | 104 | R scale |
Flexural Modulus | 23℃ | ISO 178 | 2300 | Mpa |
Flexural Strength | 23℃ | ISO 178 | 71.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.80MPa,Unannealed | ISO 75-2/Af | 79.0 | °C |
Flame retardancy | 1.50mm | UL 94 | HB | |
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 0.000090 | cm/cm/℃ |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | 220℃/10.0kg | ISO 1133 | 9.00 | cm3/10min |
Density | | ISO 1183 | 1.05 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.