ABS Stylac™ IM15 ASAHI JAPAN

Unit Price:
$4809 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.05
Melt Mass-Flow Rate		ASTM D1238/ISO 1133	7.0	g/10min

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD	ASTMD955	0.40到0.60	%
Melt Mass-Flow Rate	220°C/10.0kg	ISO1133	7.2	g/10min
Melt Volume flow Rate	220°C/10.0kg	ISO1133	7.60	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus		ISO178	2500	Mpa
Flexural Stress		ISO178	80.2	Mpa
Tensile Stress	Yield	ISO527-2/50	49.7	Mpa
Tensile Elongation		ASTM D-638	50	%
IZOD Notch Impact Strength	23℃	ASTM D-256	333	J/m
	IZOD Notch Impact Strength	0℃	ASTM D-256	196	J/m
	IZOD Notch Impact Strength	IZOD Notch Impact Strength	-30℃	ASTM D-256	108	J/m
Tensile Strength		ASTM D-638	46	Mpa
Rockwell Hardness		ASTM D-785	110	R-Scale
Flexural Modulus		ASTM D-790	2646	Mpa
Flexural Strength		ASTM D-790	74	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	84.0	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?		ASTM D-648	90	°C
Vicat Softening Temperature		ASTM D-1525	113	°C
Vicat Softening Temperature		ISO306/B	105	°C
RTIElec		UL746	60.0	°C
Evolution Calendar intelligent importer		UL746	60.0	°C
RTI		UL746	60.0	°C
Ball PressureTest		EMAC	95	°C

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Sale,2.50mm		104

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

Physical	Test Condition	Test Method	Test Result	Unit
Melt index		JIS K7210	8	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.