Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 31 | g/10min |
Density / Specific Gravity | 23°C | ISO1183 | 1.11 | g/cm³ |
Density / Specific Gravity | | ASTMD792 | 1.11 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break | ASTMD638 | 10 | % |
Flexural Modulus | | ASTMD790 | 1690 | Mpa |
Flexural Modulus | 23°C | ISO178 | 1490 | Mpa |
Flexural Strength | | ASTMD790 | 56.0 | Mpa |
Tensile Strength | | ASTMD638 | 32.0 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 40.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 10 | % |
Flexural Stress | 23°C | ISO178 | 55.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 78.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | 8E+09 | ohms |
ElectrostaticVoltage2 | 23°C | 内部方法 | 300 | V |
Half-lifeofElectrostaticVoltageDecay2 | 23°C | 内部方法 | 0.3 | sec |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179 | 15 | kJ/m² |
Notched Izod Impact Strength | 23°C,3.20mm | ASTMD256 | 100 | J/m |
Notched Izod Impact Strength | 23°C,12.7mm | ASTMD256 | 140 | J/m |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | Total,3000μm | ISO13468 | 73.0 | % |
Haze | 3000µm | ISO14782 | 17 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.