ABS CL-301 DENKA JAPAN

Unit Price:
$3823 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	1.10
Modeling Shrinkage	ASTM D955	3-5	%
Melt Mass-Flow Rate	ASTM D1238/ISO 1133	2.0	g/10min

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	2mmt		0.3-0.5	%
Haze	2mmt	ASTM D-1003	1.7	%
Transmittance	2mmt	ASTM D-1003	90	%
Flammability	垂直燃烧性	UL-94	1.5mmHB

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
IZOD Notch Impact Strength	1/4〃	ASTM D-256	164	J/m
Tensile Strength		ASTM D-638	34	Mpa
Tensile Strength	Tensile Strength		ASTM D638/ISO 527	34	kg/cm²(MPa)[Lb/in²]
Rockwell Hardness		ASTM D785	36
Rockwell Hardness	Rockwell Hardness		ASTM D-785	36	M
Flexural Modulus		ASTM D790/ISO 178	1860	kg/cm²(MPa)[Lb/in²]
Flexural Modulus	Flexural Modulus		ASTM D-790	1860	Mpa
Flexural Strength		ASTM D-790	62	Mpa
Flexural Strength	Flexural Strength		ASTM D790/ISO 178	62	kg/cm²(MPa)[Lb/in²]
Izod notch impact strength		ASTM D256/ISO 179	164	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?		ASTM D648/ISO 75	73	℃（℉）
Deflection Temperature Under Load?	Deflection Temperature Under Load?	6.4mm 1.82MPa	ASTM D-648	73	°C
Vicat Softening Temperature	5kg	JIS K-7206	82	°C
Vicat Softening Temperature	Vicat Softening Temperature		ASTM D1525/ISO R306	82	℃（℉）

Physical	Test Condition	Test Method	Test Result	Unit
Melt index	200℃×5kg	JIS K-6874	2.0	g/10min
Melt index	Melt index	220℃×10kg	JIS K-6874	26	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.