MVLDPE Daelim Poly® XP9200 Korea Daelim Basell
99
- Unit Price:
- $1302 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16 kg | ASTM D1238 | 1.5 | g/10 min |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTM D1525 | 106 | °C | |
| Peak Melting Temperature | ASTM D3418 | 116 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak Melting Temperature | 30 μm, Blown Film | 内部方法 | 95.0 | °C |
| Tensile Elongation | MD : Break, 30 μm, Blown Film | ASTM D882 | 580 | % |
| TD : Break, 30 μm, Blown Film | ASTM D882 | 620 | % | |
| Tensile Strength | MD : Break, 30 μm, Blown Film | ASTM D882 | 56.9 | Mpa |
| TD : Break, 30 μm, Blown Film | ASTM D882 | 45.1 | Mpa | |
| Gardner Impact | 30 μm, Blown Film | ASTM D1709B | 670 | g |
| Extrusion | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 150 到 190 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 30.0 μm, Blown Film | ASTM D1003 | 12 | % |
| Gloss | 45°, 30.0 μm, Blown Film | ASTM D2457 | 87 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.