PBT VALOX™ WF006N-BK1066 SABIC INNOVATIVE NANSHA
66
- Unit Price:
- $9896 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity high strength Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Home appliance components Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 14.0 | cm3/10min |
| 275°C/5.0kg | ISO1133 | 26.0 | cm3/10min | |
| Modeling Shrinkage | MD | 内部方法 | 0.12 | % |
| TD | 内部方法 | 0.28 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Break,50.0mm Span | ASTMD790 | 156 | Mpa | |
| yield | ISO527-2/5 | 2.5 | % | |
| ISO527-2/5 | 120 | Mpa | ||
| fracture | ISO527-2/5 | 120 | Mpa | |
| ISO527-2/5 | 2.5 | % | ||
| Yield | ASTMD638 | 110 | Mpa | |
| Break | ASTMD638 | 110 | Mpa | |
| 50.0mm Span | ASTMD790 | 6600 | Mpa | |
| --7 | ISO178 | 7400 | Mpa | |
| --8 | ISO178 | 166 | Mpa | |
| --1 | ASTMD638 | 7900 | Mpa | |
| Yield | ASTMD638 | 2.7 | % | |
| Break | ASTMD638 | 2.7 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | ASTMD152514 | 153 | °C | |
| ISO306/B50 | 157 | °C | ||
| Flow:-40 to 40°C | ASTME831 | 2.1E-05 | cm/cm/°C | |
| ISO11359-2 | 2.2E-05 | cm/cm/°C | ||
| Flow:23 to 80°C | ISO11359-2 | 1.6E-05 | cm/cm/°C | |
| ASTME831 | 1.5E-05 | cm/cm/°C | ||
| Flow:-40 to 40°C | ASTME831 | 7.9E-05 | cm/cm/°C | |
| ISO11359-2 | 8.2E-05 | cm/cm/°C | ||
| Flow:23 to 80°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| ASTME831 | 4.5E-05 | cm/cm/°C | ||
| 1.8MPa, Unannealed,6.40mm | ASTMD648 | 175 | °C | |
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 158 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 1.10GHz | 内部方法 | 0.012 | |
| 1.90GHz | 内部方法 | 0.011 | ||
| Dielectric Constant | 1.10GHz | 内部方法 | 3.53 | |
| 1.90GHz | 内部方法 | 3.54 | ||
| Volume Resistivity | ASTMD257 | 1.1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/2U | 62 | kJ/m² |
| 23°C12 | ISO180/1U | 52 | kJ/m² | |
| -30°C | ASTMD256 | 120 | J/m | |
| -30°C10 | ISO180/1A | 11 | kJ/m² | |
| 23°C11 | ISO180/1A | 14 | kJ/m² | |
| 23°C | ASTMD256 | 170 | J/m | |
| ASTMD4812 | 840 | J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.