PC/ABS CYCOLOY™ CY4000-7M1A4447 SABIC INNOVATIVE NANSHA
73
- Unit Price:
- $4912 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength Aging resistance
- Application Areas:Electronic and electrical Shell
- Color:--
- Grade:High liquidity level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 260℃ 2.16kg | ASTM D1238 | 23 | g/10min |
| 260℃ 2.16kg | ISO 1133 | 21 | g/10min | |
| proportion | ISO 1183 | 1.2 | g/cm³ | |
| Modeling Shrinkage (Across Flow) | ISO 294 | 0.6 | % | |
| Modeling Shrinkage (Flow) | ISO 294 | 0.4 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23℃ | ISO 180 | 10 | kJ/m² |
| -30℃ | ISO 180 | 10 | kJ/m² | |
| Coefficient of Linear Thermal Expansion | ISO 11359 | 0.000080 | cm/cm/℃ | |
| Taber Abrasion Resistance | 1kg | 15 | mg/1000cy | |
| Deflection Temperature Under Load? | Unannealed0.45MPa | ISO 75 | 85 | °C |
| Unannealed1.8MPa | ISO 75 | 72 | °C | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 10 | kJ/m² |
| -30℃ | ISO 179 | 10 | kJ/m² | |
| Vicat Softening Temperature | 50℃/hr 50N | ISO 306 | 85 | °C |
| 120℃/hr 50N | ISO 306 | 90 | °C | |
| Tensile Modulus | 23℃ | ISO 527 | 2700 | Mpa |
| Tensile Strength | Yield23℃ | ISO 527 | 55 | Mpa |
| 23℃ 50mm/min | ISO 527 | 45 | Mpa | |
| Tensile Elongation | Yield23℃ 50mm/min | ISO 527 | 3 | % |
| 23℃ | ISO 527 | 40 | % | |
| Flexural Modulus | 23℃ | ISO 178 | 2500 | Mpa |
| Flexural Strength | Yield23℃ | ISO 178 | 85 | Mpa |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Constant | 1MHz | IEC 60250 | 2.7 | |
| IEC 60250 | 2.7 | |||
| Insulation strength | 3.2mm | IEC 60243 | 17 | KV/mm |
| Volume Resistivity | IEC 60093 | 1000000000000000 | Ω.cm | |
| Surface resistance | IEC 60093 | 1000000000000000 | ||
| CTI | IEC 60112 | 600 | V | |
| Dissipation Factor | IEC 60250 | 0.006 | ||
| Dissipation Factor | IEC 60250 | 0.006 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO 2039 | 110 | Mpa |
| Flame Rating | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Ignition Temperature | 3.2mm | IEC 60695 | 960 | °C |
| Oxygen Index | ISO 4589 | 29 | % | |
| Fire rating | 2.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 |
| UL | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | 2.5mm | UL746B | 60 | °C |
| Fire rating | 2.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 | ||
| RTI Elec | 3.0mm | UL 746B | 60 | °C |
| RTI Imp | 2.5mm | UL746B | 60 | °C |
| 3.0mm | UL746B | 60 | °C | |
| RTI Str | 2.5mm | UL746B | 60 | °C |
| 3.0mm | UL746B | 60 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.