PC/ABS CYCOLOY™ LG9000 BK1065S SABIC INNOVATIVE NANSHA

Unit Price:
$4358 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Moisture Absorption	24 hr	ASTM D570	0.10	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C	ASTM D570	0.40	%
Melt Mass-Flow Rate	260°C/5.0 kg	ASTM D1238	17	g/10 min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTM D638	75	%
Flexural Modulus	50.0 mm Span	ASTM D790	2300	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	84.0	Mpa
Tensile Strength	Yield	ASTM D638	54.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTM D15254	129	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	123	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	129	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	107	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	110	°C
Linear thermal expansion coefficient	Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
Thermal Conductivity		ASTM C177	0.20	W/m/K
RTI		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
RTI Elec		UL 746	60.0	°C

Electrical performance	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 2
Hot-wire Ignition	UL 746	PLC 2
High Amp Arc Ignition	UL 746	PLC 0
Arc Resistance	ASTM D495	PLC 6

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	30 到 80	%
Rear Temperature	250 到 290	°C
Middle Temperature	255 到 295	°C
Front Temperature	260 到 300	°C
Nozzle Temperature	275 到 300	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.038 到 0.076	mm
Drying Temperature	105 到 110	°C
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	275 到 300	°C
Mold Temperature	60 到 90	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	-30°C, Total Energy	ASTM D3763	33.0	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	40.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Gardner	60°, 无织构	ASTM D523	30

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.