Material Description

Technical Data Sheet

Material Description

Material Properties:Low temperature resistanc Easy to process High mobility UV resistance
Application Areas:Electrical field Electronic field Household appliances Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.40 到 0.80	%
	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.40 到 0.80	%
		Modeling Shrinkage	MD：3.20mm	内部方法	0.40to0.80	%
		Modeling Shrinkage	Modeling Shrinkage	TD：3.20mm	内部方法	0.40to0.80	%
Moisture Absorption	Saturation,23°C	ISO62	0.35	%
	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.15	%
		Moisture Absorption	Saturation, 23°C	ISO 62	0.12	%
		Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.090	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	17	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	16.0	cm3/10min
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	20	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	19.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Strength		ISO178	85.0	Mpa
Flexural Stress	-- 5, 6	ISO 178	89.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	94.0	Mpa
Tensile Elongation	Yield	ASTMD638	5.8	%
Tensile Modulus		ASTMD638	2280	Mpa
Tensile Strength	Break	ASTMD638	58.7	Mpa
Tensile Strength	Tensile Strength	Yield	ASTMD638	58.1	Mpa
Flexural Modulus	50.0mmSpan	ASTMD790	2320	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	95.1	Mpa
Tensile Stress	Break	ISO527-2/50	55.0	Mpa
Tensile Stress	Tensile Stress	Yield	ISO527-2/50	57.0	Mpa
Tensile Strain	Yield	ISO527-2/50	5.0	%
Tensile Strain	Tensile Strain	Break	ISO527-2/50	100	%
Tensile Modulus	-- 2	ASTM D638	2260	Mpa
	Tensile Modulus	--	ISO 527-2/1	2340	Mpa
	Tensile Modulus	Tensile Modulus		ISO527-2/1	2150	Mpa
Tensile Elongation	Yield 3	ASTM D638	5.7	%
	Tensile Elongation	Yield	ISO 527-2/50	5.4	%
		Tensile Elongation	Break 3	ASTM D638	120	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	120	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2240	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2140	Mpa
Tensile Strength	Yield 3	ASTM D638	58.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	57.0	Mpa
		Tensile Strength	Break 3	ASTM D638	57.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	56.0	Mpa
Flexural Modulus		ISO178	2240	Mpa
Tensile Elongation	Break	ASTMD638	110	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Heat Deflection Temperature	0.45MPa,Annealed	ISO75-2/Be	136	°C
Heat Deflection Temperature	1.8MPa,Unannealed,100mmSpan	ISO75-2/Ae	125	°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	121	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	116	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过
Vicat Softening Temperature		ASTMD152511	144	°C
	Vicat Softening Temperature	--	ISO306/B50	144	°C
		Vicat Softening Temperature	--	ISO306/B120	145	°C
			Vicat Softening Temperature	--	ASTM D152510, ISO 306/B5010	138	°C
			Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	139	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	137	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	124	°C
RTIElec		UL746	130	°C
Evolution Calendar intelligent importer		UL746	120	°C
RTIStr		UL746	125	°C
Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	7.2E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD：23to80°C	ISO11359-2	7.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	7.6E-05	cm/cm/°C
			Linear thermal expansion coefficient	TD：23to80°C	ISO11359-2	7.5E-05	cm/cm/°C
				Linear thermal expansion coefficient	Flow : -40 to 95°C	ASTM E831	7.5E-5	cm/cm/°C
					Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	7.5E-5	cm/cm/°C
						Linear thermal expansion coefficient	Across Flow : -40 to 95°C	ASTM E831	7.6E-5	cm/cm/°C
						Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	7.6E-5	cm/cm/°C
RTI		UL 746	130	°C
RTI Elec		UL 746	130	°C
Ball PressureTest	125°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		ASTM D257	> 1.0E+15	ohms
Volume Resistivity		ASTM D257	> 1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	295 到 315	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	270 到 295	°C
Middle Temperature	280 到 305	°C
Front Temperature	295 到 315	°C
Nozzle Temperature	290 到 310	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	74.0	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	69.6	J
Charpy Notched Impact Strength	-30°C	ISO179/1eA	25	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	60	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Notched Izod Impact Strength	-30°C	ISO180/1A	20	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	55	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	45	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Unnotched Izod Impact Strength	-30°C	ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO 180/1U	无断裂
Unnotched Izod Impact Strength	-30°C	ISO180/1U	NoBreak
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO180/1U	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	L -Sale	ISO 2039-2	89
Ball Indentation Hardness	H358/30	ISO2039-1	95.0	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Haze	2540 µm	ASTM D1003	3.0	%
Transmittance	2540 µm	ASTM D1003	82.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0mm	IEC60695-2-12	850	°C
	Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0 mm	IEC 60695-2-12	960	°C
Flame Rating	1.5 mm	UL 94	HB
Oxygen Index		ISO4589-2	32	%
Glow Wire Ignition Temperature	0.8 mm	IEC 60695-2-13	850	°C
	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	850	°C
		Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	875	°C
		Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	875	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.