Need Help? Contact Us service@plas.com
Get App

PC LEXAN™  FXE1414L WH9E455L SABIC INNOVATIVE NANSHA

67
  • Unit Price:
    $3666 USD/MT
  • Packaging Specification:
    25 KG/PKG
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading:
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description
Technical Data Sheet

Material Description

  • Material Properties:Low temperature resistanc transparent Flame retardant
  • Application Areas:Electrical field Electrical appliances Electronic field Household appliances
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

Physical PropertiesTest ConditionTest MethodTest ResultUnit
Melt Mass-Flow Rate300°C/1.2 kgASTM D123811g/10 min
Melt Volume flow Rate300°C/1.2 kgISO 113310.0cm3/10min
Moisture AbsorptionSaturation, 23°CISO 620.17%
Moisture AbsorptionEquilibrium, 23°C, 50% RHISO 620.070%
Modeling Shrinkage - Flow3.20 mm内部方法0.40 到 0.80%
Mechanical PropertiesTest ConditionTest MethodTest ResultUnit
Tensile Modulus-- 2ASTM D6382030Mpa
Tensile Modulus--ISO 527-2/12000Mpa
Tensile ElongationYield 3ASTM D6385.0%
Tensile ElongationYieldISO 527-2/505.0%
Tensile ElongationBreak 3ASTM D63884%
Tensile ElongationBreakISO 527-2/5075%
Flexural Modulus50.0 mm Span 4ASTM D7902050Mpa
Flexural Modulus-- 5ISO 1782110Mpa
Tensile StrengthYield 3ASTM D63852.0Mpa
Tensile StrengthYieldISO 527-2/5052.0Mpa
Tensile StrengthBreak 3ASTM D63854.0Mpa
Tensile StrengthBreakISO 527-2/5047.0Mpa
Flexural Stress-- 5, 6ISO 17883.0Mpa
Flexural StressYield, 50.0 mm Span 4ASTM D79086.0Mpa
Thermal PropertiesTest ConditionTest MethodTest ResultUnit
Vicat Softening Temperature--ASTM D15259, ISO 306/B509138°C
Vicat Softening Temperature--ISO 306/B120146°C
Linear thermal expansion coefficientFlow : -40 to 40°CASTM E831, ISO 11359-27.0E-5cm/cm/°C
Linear thermal expansion coefficientAcross Flow : -40 to 40°CASTM E8316.7E-5cm/cm/°C
Linear thermal expansion coefficientAcross Flow : -40°CISO 11359-28.2E-5cm/cm/°C
Deflection Temperature Under Load?1.8 MPa, Unannealed, 3.20 mmASTM D648121°C
Deflection Temperature Under Load?1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8ISO 75-2/Af118°C
InjectionTest ConditionTest MethodTest ResultUnit
Drying Time3.0 到 4.0hr
Rear Temperature260 到 280°C
Middle Temperature280 到 305°C
Front Temperature295 到 315°C
Nozzle Temperature290 到 310°C
Hopper Temperature60 到 80°C
Drying Temperature120°C
Suggested Max Moisture0.020%
Processing (Melt) Temp295 到 315°C
Mold Temperature70 到 95°C
Impact PropertiesTest ConditionTest MethodTest ResultUnit
Instrumented Dart Impact23°C, Total EnergyASTM D376368.0J
FlammabilityTest ConditionTest MethodTest ResultUnit
Flame Rating0.40 mmUL 94HB
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.