Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 14 | g/10min |
Density | | ISO1183 | 1.18 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strain | 断裂 | ISO527-2/50 | >100 | % |
Tensile Strain | 屈服 | ISO527-2/50 | 5.7 | % |
Tensile Modulus | | ASTMD638 | 2330 | Mpa |
Tensile Elongation | 屈服 | ASTMD638 | 6.0 | % |
Tensile Elongation | 断裂 | ASTMD638 | 85 | % |
Tensile Strength | 屈服 | ASTMD638 | 64.0 | Mpa |
Tensile Strength | 断裂 | ASTMD638 | 62.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | -- | ISO306/B50 | 134 | °C |
Vicat Softening Temperature | -- | ISO306/B120 | 135 | °C |
Deflection Temperature Under Load? | 1.8MPa,未退火,6.40mm | ASTMD648 | 118 | °C |
Linear thermal expansion coefficient | MD:-40到40°C | ISO11359-2 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40到40°C | ISO11359-2 | 7E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 0.0to4.0E+16 | ohms |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 | kJ/m² |
Charpy Notched Impact Strength | 0°C | ISO179/1eA | 17 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 28 | kJ/m² |
Notched Izod Impact Strength | -30°C | ASTMD256 | 220 | J/m |
Notched Izod Impact Strength | 0°C | ASTMD256 | 530 | J/m |
Notched Izod Impact Strength | 23°C | ASTMD256 | 800 | J/m |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ISO4589-2 | 32 | % |
Glow Wire Ignition Temperature | 0.75mm | IEC60695-2-13 | 775 | °C |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 775 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 775 | °C |
GlowWireFlammability | 0.75mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.