ABS CYCOLAC™ FR15U SABIC INNOVATIVE US

Unit Price:
$4784 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.20mm	内部方法	0.50to0.70	%
Melt Mass-Flow Rate	230°C/3.8kg	ASTMD1238	3.3	g/10min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	220°C/5.0kg	ISO1133	7.0	g/10min
Melt Volume flow Rate	220°C/10.0kg	ISO1133	40.0	cm3/10min
Melt Viscosity	200°C,1000sec^-1	ASTMD3835	320	Pa·s
Density / Specific Gravity		ASTMD792	1.19	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.19	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Yield	ASTMD638	2.4	%
Tensile Modulus		ASTMD638	2070	Mpa
Tensile Strength	Yield	ASTMD638	37.9	Mpa
Tensile Strength	Tensile Strength	Break	ASTMD638	30.3	Mpa
Flexural Modulus	50.0mmSpan	ASTMD790	2340	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	67.6	Mpa
Tensile Elongation	Break	ASTMD638	17	%
Flexural Modulus		ISO178	2260	Mpa
Flexural Strength		ISO178	63.3	Mpa
Tensile Modulus		ISO527-2/1	2210	Mpa
Tensile Stress	Yield	ISO527-2/50	41.1	Mpa
Tensile Strain	Break	ISO527-2/50	22	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTIElec		UL746	90.0	°C
Evolution Calendar intelligent importer		UL746	85.0	°C
RTIStr		UL746	90.0	°C
Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	9E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	9.2E-05	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	86.1	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	75.0	°C
Vicat Softening Temperature		ASTMD15258	93.9	°C
Vicat Softening Temperature	Vicat Softening Temperature		ISO306/B50	92.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Hot-wire Ignition	HWI	UL746	PLC2
High Amp Arc Ignition	HAI	UL746	PLC4
High Voltage Arc Tracking Rate	HVTR	UL746	PLC4
Volume Resistivity		IEC60093	>1.0E+14	ohms·cm
Comparative Tracking Index	CTI	UL746	PLC1
Dielectric Strength	3.20mm,in Oil	IEC60243-1	20	KV/mm
Arc Resistance		ASTMD495	PLC7

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	23°C	ASTMD256	210	J/m
Notched Izod Impact Strength	23°C	ISO180/1A	12	kJ/m²
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	28.5	J

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	2.8mm	UL94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.