ABS CYCOLAC™ MG47F-NA1000 SABIC INNOVATIVE US

Unit Price:
$1923 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	230°C/3.8 kg	ASTM D1238	5.6	g/10 min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	220°C/10.0 kg	ISO 1133	18	g/10 min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 1	ASTM D638	2270	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2370	Mpa
Tensile Elongation	Yield 2	ASTM D638	2.0	%
	Tensile Elongation	Yield	ISO 527-2/50	2.6	%
		Tensile Elongation	Break 2	ASTM D638	24	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	25	%
Flexural Modulus	50.0 mm Span 3	ASTM D790	2300	Mpa
Flexural Modulus	Flexural Modulus	-- 4	ISO 178	2200	Mpa
Tensile Strength	Yield 2	ASTM D638	44.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	47.0	Mpa
		Tensile Strength	Break 2	ASTM D638	33.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	35.0	Mpa
Flexural Stress	-- 4, 5	ISO 178	70.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 3	ASTM D790	70.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
RTI Elec		UL 746	60.0	°C
Vicat Softening Temperature	--		99.0	°C
	Vicat Softening Temperature	--	ISO 306/B50	98.0	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	100	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	8.8E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	8.8E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	94.0	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	80.0	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 7	ISO 75-2/Af	81.0	°C

Electrical performance	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 0
Hot-wire Ignition	UL 746	PLC 3
High Voltage Arc Tracking Rate	UL 746	PLC 3
Arc Resistance	ASTM D495	PLC 6
High Amp Arc Ignition	UL 746	PLC 0

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Melt Viscosity	240°C, 1000 sec^-1	ASTM D3835	225	Pa·s

Injection	Test Result	Unit
Drying Temperature	80 到 95	°C
Suggested Max Moisture	0.10	%
Processing (Melt) Temp	220 到 260	°C
Mold Temperature	50 到 70	°C
Drying Time	2.0 到 4.0	hr
Suggested Shot Size	50 到 70	%
Rear Temperature	190 到 210	°C
Middle Temperature	205 到 225	°C
Front Temperature	215 到 240	°C
Nozzle Temperature	220 到 260	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	30 到 60	rpm
Vent Depth	0.038 到 0.051	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	30.0	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	26	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	112

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.