PPS FORTRON® 1140L4 SD3002 CELANESE USA

240

Unit Price:
$7247 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
232MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant High temperature resistan enhance Glass fiber reinforced Injection grade Medium melt viscosity
Application Areas:Fiber grade Slight flash During injection molding
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	0.40到0.60	%
	Shrinkage rate	MD	ISO294-4	0.20到0.60	%
		Shrinkage rate	MD	ASTMD955	0.20到0.30	%
		Shrinkage rate	Shrinkage rate	TD	ASTMD955	0.50到0.70	%
Water absorption rate	Saturation,23°C	ISO62	0.020	%
Mold shrinkage rate		ISO 294-4	0.2-0.6	%
Specific volume		ASTMD792	0.611	cm³/g
Density/specific gravity		ASTMD792,ISO1183	1.65	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress 3		ISO178	285	Mpa
IZOD notch impact strength		ISO 180/1A	10	kJ/m²
Tensile strength	Break,23°C	ASTMD638	200	Mpa
Tensile strength	Tensile strength	Break	ISO527-2/1A/5	195	Mpa
Tensile modulus		ISO 527	14700	Mpa
	Tensile modulus	-40°C	ASTMD638	14500	Mpa
		Tensile modulus	75°C	ASTMD638	11900	Mpa
			Tensile modulus	150°C	ASTMD638	4270	Mpa
				Tensile modulus	200°C	ASTMD638	3240	Mpa
				Tensile modulus	Tensile modulus	--	ISO527-2/1A/1	14700	Mpa
tensile strength		ISO 527	195	Mpa
elongation	Break,23°C	ASTMD638	1.7	%
elongation	elongation	Break	ISO527-2/1A/5	1.9	%
Rockwell hardness		ASTM-D785	100	R-Scale
Bending modulus	23°C	ISO178	14500	Mpa
Bending modulus	Bending modulus		ISO 178	14500	Mpa
bending strength		ISO 178	285	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.80Mpa	ISO 75-A	270	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTMD648	280	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	265	°C
			Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	270	°C
			Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	215	°C
Flame retardant grade		UL94	V-0
Linear coefficient of thermal expansion	MD	ISO11359-2	2.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	4.2E-05	cm/cm/°C
Glass transition temperature 4		ISO11357-2	90.0	°C
Melting temperature 4		ISO11357-3	280	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor	1kHz	ASTMD150	1E-03
	Dissipation factor	1MHz	ASTMD150	1E-03
	Dissipation factor	Dissipation factor	1MHz	IEC60250	6.2E-03
Leakage Trace Index		IEC60112	125	V
Dielectric strength		IEC60243-1	28	KV/mm
Surface resistivity		IEC60093	>1.0E+15	ohms
Dielectric constant	1kHz	ASTMD150	3.50
	Dielectric constant	1MHz	ASTMD150	3.50
	Dielectric constant	Dielectric constant	1MHz	IEC60250	4.60
Arc resistance		ASTMD495	134	sec
Volume resistivity	--	ASTMD257	1E+16	ohms·cm
Volume resistivity	Volume resistivity	--	IEC60093	>1.0E+15	ohms·cm

Filling analysis	Test Condition	Test Method	Test Result	Unit
SpecificHeatCapacity of Melt		内部方法	1500	J/kg/°C

Biochemical properties	Test Condition	Test Method	Test Result	Unit
Filling amount			40	%

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	10	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO180/1A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	10	kJ/m²
Unscented Izod impact strength	23°C	ISO180/1U	34	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	53	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	53	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTMD785	100
Rockwell hardness	Rockwell hardness	M-Sale	ISO2039-2	100

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
	UL flame retardant rating	1.5mm	UL94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Extreme Oxygen Index		ISO4589-2	47	%

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate		ASTM-D570	0.02	%
Density/specific gravity		ISO 1183	1.65	g/cm³

Supplementary Information	Test Condition	Test Method	Test Result	Unit
SpecimensThickness Shrinkage		内部方法	3.18	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.