Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Saturation,23℃ Saturation,23℃ | ISO 62 | 0.65 | % |
Density | | ISO 1183 | 1.41 | g/cm³ |
Melt Volume flow Rate | 190℃,2.16 kg 190℃/2.16 kg | ISO 1133 | 24 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | 23℃ 23℃ | ISO 178 | 2600 | Mpa |
Tensile Strain | Yield Yield | ISO 527-2/1A/50 | 7.5 | % |
Tensile Strength | Yield Yield | ISO 527-2/1A/50 | 64 | Mpa |
Nominal Tensile Strain at Break | | ISO 527-2/1A/50 | 17 | % |
Tensile Modulus | | ISO 527-2/1A/1 | 2750 | Mpa |
Tensile Creep Modulus | 1000 hr 1000 hr | ISO 899-1 | 1200 | Mpa |
Tensile Creep Modulus(1 hr) | | ISO 899-1 | 2400 | Mpa |
Electrical | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC 60243-1 | 35 | KV/mm |
Comparative Tracking Index | | IEC 60112 | 600 | V |
Surface Resistivity | | IEC 60093 | 100000000000000 | ohms |
Volume Resistivity | | IEC 60093 | 100000000000000 | ohms·cm |
Relative Permittivity | 100 Hz 100 Hz | IEC 60250 | 4 | |
Relative Permittivity | 1 MHz 1 MHz | IEC 60250 | 4 | |
Dissipation Factor | 100 Hz 100 Hz | IEC 60250 | 0.002 | |
Dissipation Factor | 1 MHz 1 MHz | IEC 60250 | 0.005 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30℃ -30°C | ISO 179/1eU | 120 | kJ/m² |
Charpy Unnotched Impact Strength | 23℃ 23°C | ISO 179/1eU | 120 | kJ/m² |
Thermal | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | TD TD | ISO 11359-2 | 0.00011 | 1/℃ |
Coefficient of Linear Thermal Expansion | MD MD | ISO 11359-2 | 0.00011 | 1/℃ |
Melting Temperature | | ISO 11357-3 | 164 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.