POM HOSTAFORM® C9021GV1/10 CELANESE GERMANY

Unit Price:
$6725 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.48

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength(Yield)	50mm/min	ISO 527 part 1/2	65	Mpa
Ball Indentation Hardness	30sec数值	ISO 2039 part 1	140	Mpa
Tensile Elongation?(Break)	50mm/min	ISO 527 part 1/2	20	%
Tensile Modulus	1mm/min	ISO 527 part 1/2	2800	Mpa
Tensile Modulus	Tensile Modulus		ASTM D638/ISO 527	696000	kg/cm²(MPa)[Lb/in²]
Tensile Elongation	伸长率	ISO 527 part 1/2	9.0	%
Flexural Modulus		ISO 178	2700	Mpa
Flexural Modulus	Flexural Modulus		ASTM D790/ISO 178	653000	kg/cm²(MPa)[Lb/in²]
Tensile Creep Modulus	1 hour	ISO 899 part 1	2400	Mpa
Tensile Creep Modulus	Tensile Creep Modulus	1000 hours	ISO 899 part 1	1200	Mpa
Charpy Notched Impact Strength	23℃	ISO 179 1eA	0.6	J/cm
Charpy Notched Impact Strength	Charpy Notched Impact Strength	低温-30℃	ISO 179 1eA	0.6	J/cm
Charpy Unnotched Impact Strength	低温-30℃	ISO 179 1eU	12	J/cm
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23℃	ISO 179 1eU	12.0	J/cm

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa	ISO 75 part 1/2	100	°C
Melting Temperature	DSC,10 K/min	ISO 3146 method C1b	166	°C
Vicat Softening Temperature		ASTM D1525/ISO R306	313	℃（℉）
Vicat Softening Temperature	Vicat Softening Temperature	VST/B/50	ISO 306	150	°C
Coefficient of Linear Thermal Expansion	23-55℃ Longitudinal	ISO 11359 part 1/2	110	µm/m-℃

Electrical performance	Test Condition	Test Method	Test Result	Unit
Insulation strength		IEC 60243 part 1	35	KV/mm
Dielectric Constant	1 MHz	IEC 60250	4.20
Dielectric Constant	Dielectric Constant	低频100 Hz	IEC 60250	4.20
Dissipation Factor?		IEC 60250	0.008	1 MHz
Dissipation Factor?	Dissipation Factor?	低频100 Hz	IEC 60250	0.0025

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	23℃and50%RH	ISO 62	0.2	%
Moisture Absorption	Moisture Absorption	Saturation23℃	ISO 62	0.75	%
Melt index	8.5cm	ISO 1133	12.07	g/10min
Density		ISO 1183	1.42	g/cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.