PPO NORYL GTX™ GTX934 74701 SABIC INNOVATIVE US
72
- Unit Price:
- $5339 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance High temperature resistan Dimensional stability High mobility
- Application Areas:Electrical applications Industrial machinery
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 13 | g/10min |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 13.0 | cm3/10min |
| Modeling Shrinkage | MD2 | 内部方法 | 1.6到2.0 | % |
| MD:3.20mm | 内部方法 | 1.4到1.7 | % | |
| TD:3.20mm | 内部方法 | 1.1到1.4 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 3.5 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.2 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | --3 | ASTMD638 | 2300 | Mpa |
| -- | ISO527-2/1 | 2400 | Mpa | |
| Tensile Strength | Yield4 | ASTMD638 | 65.0 | Mpa |
| Yield | ISO527-2/50 | 65.0 | Mpa | |
| Break4 | ASTMD638 | 55.0 | Mpa | |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| Tensile Elongation | Yield4 | ASTMD638 | 5.0 | % |
| Yield | ISO527-2/50 | 4.5 | % | |
| Break4 | ASTMD638 | 60 | % | |
| Break | ISO527-2/50 | 25 | % | |
| Flexural Modulus | 50.0mmSpan5 | ASTMD790 | 2350 | Mpa |
| --6 | ISO178 | 2200 | Mpa | |
| Flexural Stress | --6,7 | ISO178 | 90.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 95.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal Conductivity | ISO8302 | 0.23 | W/m/K | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 190 | °C |
| 0.45MPa,Unannealed,100mmSpan10 | ISO75-2/Be | 190 | °C | |
| Vicat Softening Temperature | -- | ASTM D-596 | 205 | °C |
| -- | ISO306/A50 | 250 | °C | |
| -- | ISO306/B50 | 200 | °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 | |
| Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD:23to60°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 8.5E-05 | cm/cm/°C | |
| TD:23to60°C | ISO11359-2 | 7E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 20 | kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 60.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 85.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.