PPO NORYL™ GFN30-701S SABIC INNOVATIVE SHANGHAI

Unit Price:
$4784 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	0.10	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.040	%
Melt Mass-Flow Rate	280°C/5.0 kg	ASTM D1238	3.2	g/10 min
Melt Volume flow Rate	280°C/5.0 kg	ISO 1133	2.00	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.10 到 0.40	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	160	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	160	Mpa
Tensile Modulus	-- 2	ASTM D638	8600	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	8200	Mpa
Tensile Elongation	Break 3	ASTM D638	3.0	%
Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	2.5	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	7200	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	6800	Mpa
Tensile Strength	Break 3	ASTM D638	130	Mpa
Tensile Strength	Tensile Strength	Break	ISO 527-2/50	110	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D15259, ISO 306/B509	147	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	149	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	2.1E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : -40 to 40°C	ISO 11359-2	2.3E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	7.0E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	147	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	139	°C

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	30 到 70	%
Rear Temperature	265 到 315	°C
Middle Temperature	275 到 320	°C
Front Temperature	290 到 325	°C
Nozzle Temperature	300 到 325	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	20 到 100	rpm
Drying Temperature	110 到 120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	300 到 325	°C
Mold Temperature	80 到 110	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	590	J/m
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 8	ISO 180/1U	30	kJ/m²
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	20.0	J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.