PPO NORYL™ NH6020-100 SABIC INNOVATIVE NETHERLANDS

Unit Price:
$3744 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan High mobility Glass fiber reinforced
Application Areas:Electrical applications Automotive interior parts
Color:--
Grade:Flame retardant grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.20mm	内部方法	0.50到0.70	%
Moisture Absorption	饱和,23°C	ISO62	0.18	%
Moisture Absorption	Moisture Absorption	平衡,23°C,50%RH	ISO62	0.060	%
Melt Mass-Flow Rate	280°C/5.0kg	ASTMD1238	14	g/10min
Melt Volume flow Rate	280°C/5.0kg	ISO1133	11.6	cm3/10min
Density		ASTMD792,ISO1183	1.14	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	--6,7	ISO178	114	Mpa
Flexural Stress	Flexural Stress	屈服,50.0mm跨距5	ASTMD790	121	Mpa
Tensile Strength	断裂4	ASTMD638	67.6	Mpa
	Tensile Strength	断裂	ISO527-2/50	56.6	Mpa
		Tensile Strength	屈服4	ASTMD638	78.9	Mpa
		Tensile Strength	Tensile Strength	屈服	ISO527-2/50	77.4	Mpa
Tensile Modulus	--3	ASTMD638	2740	Mpa
Tensile Modulus	Tensile Modulus	--	ISO527-2/1	2740	Mpa
Tensile Elongation	屈服	ISO527-2/50	4.6	%
	Tensile Elongation	断裂4	ASTMD638	6.1	%
		Tensile Elongation	断裂	ISO527-2/50	4.2	%
		Tensile Elongation	Tensile Elongation	屈服4	ASTMD638	4.6	%
Flexural Modulus	50.0mm跨距5	ASTMD790	3020	Mpa
Flexural Modulus	Flexural Modulus	--6	ISO178	2690	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,未退火,3.20mm	ASTMD648	125	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,未退火,64.0mm跨距10	ISO75-2/Af	125	°C
RTIElec		UL746	110	°C
Evolution Calendar intelligent importer		UL746	105	°C
Linear thermal expansion coefficient	MD:-40到40°C	ASTME831	7.8E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD:-40到40°C	ISO11359-2	7.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD:-40到40°C	ASTME831	7E-06	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD:-40到40°C	ISO11359-2	7.8E-05	cm/cm/°C
Vicat Softening Temperature	--	ASTMD152511	150	°C
	Vicat Softening Temperature	--	ISO306/B50	141	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	151	°C
RTI		UL746	110	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	1.60mm,在油中	IEC60243-1	27	KV/mm
Comparative Tracking Index		IEC60112	600	V
Volume Resistivity		IEC60093	2.5E+16到4.2E+16	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	18.4	J
Charpy Notched Impact Strength	23°C	ISO179/1eA	9.8	kJ/m²
Notched Izod Impact Strength	-30°C	ASTMD256	36	J/m
	Notched Izod Impact Strength	23°C	ASTMD256	49	J/m
		Notched Izod Impact Strength	-30°C9	ISO180/1A	5.4	kJ/m²
		Notched Izod Impact Strength	Notched Izod Impact Strength	23°C9	ISO180/1A	8.1	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.0mm	IEC60695-2-12	960	°C
Oxygen Index		ISO4589-2	37	%
Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	825	°C
	Glow Wire Ignition Temperature	2.0mm	IEC60695-2-13	800	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	800	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.