PPO NORYL GTX™ PPX830 SABIC INNOVATIVE SHANGHAI
783
- Unit Price:
- $3989 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability High impact High rigidity
- Application Areas:Printer components Cold water pipe applicati Water heater
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.25 | % |
| TD：3.20mm | 内部方法 | 0.40to0.60 | % | |
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 6.0 | g/10min |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 6.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | ISO178 | 141 | Mpa | |
| Tensile Modulus | ISO527-2/1 | 7700 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 100 | % |
| Flexural Modulus | ISO178 | 7100 | Mpa | |
| Tensile Stress | Yield | ISO527-2/5 | 98.0 | Mpa |
| Break | ISO527-2/5 | 98.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 3.2 | % |
| Break | ISO527-2/5 | 3.2 | % | |
| Tensile Elongation | Yield | ASTMD638 | 2.9 | % |
| Tensile Modulus | ASTMD638 | 7600 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 101 | Mpa |
| Yield | ASTMD638 | 101 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 6600 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 144 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | TD：-30to80°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| MD：-40to95°C | ASTME831 | 2.5E-05 | cm/cm/°C | |
| MD：-30to80°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| TD：-40to95°C | ASTME831 | 1.3E-04 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 166 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 156 | °C | |
| Vicat Softening Temperature | ISO306/B120 | 150 | °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 153 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 168 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 36 | kJ/m² |
| 23°C | ISO179/1eU | 39 | kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 10 | kJ/m² |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 42 | kJ/m² |
| 23°C | ISO180/1U | 42 | kJ/m² | |
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 10.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 15.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.0mm | UL94 | HB | |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 650 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.