PPO NORYL™ SE10000 SABIC INNOVATIVE SHANGHAI
81
- Unit Price:
- $3496 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Hydrolysis resistance
- Application Areas:Household appliances Automotive components
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD2 | 内部方法 | 0.50to0.70 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.060 | % |
| Melt Mass-Flow Rate | 280°C/5.0kg | ASTMD1238 | 8.5 | g/10min |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 8.70 | cm3/10min |
| Outdoor Suitability | UL746C | f1 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ASTMD638 | 2500 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 53.1 | Mpa |
| Flexural Modulus | ISO178 | 2560 | Mpa | |
| Flexural Strength | ISO178 | 99.5 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 61.3 | Mpa |
| Break | ISO527-2/50 | 50.8 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 4.3 | % |
| Break | ISO527-2/50 | 21 | % | |
| Tensile Modulus | ISO527-2/1 | 2670 | Mpa | |
| Flexural Modulus | 50.0mmSpan5 | ASTMD790 | 2700 | Mpa |
| 100mmSpan6 | ASTMD790 | 2400 | Mpa | |
| Flexural Strength | Yield,50.0mmSpan5 | ASTMD790 | 100 | Mpa |
| Yield,100mmSpan6 | ASTMD790 | 98.0 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 15 | % |
| Yield | ASTMD638 | 4.0 | % | |
| Tensile Strength | Yield | ASTMD638 | 65.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 127 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 129 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 113 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 118 | °C | |
| RTIElec | UL746 | 110 | °C | |
| Evolution Calendar intelligent importer | UL746 | 105 | °C | |
| RTIStr | UL746 | 110 | °C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 129 | °C |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 115 | °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 132 | °C |
| -- | ISO306/B120 | 135 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 8E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 8.8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 18 | KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC1 | |
| Arc Resistance | ASTMD495 | PLC6 | ||
| Dissipation Factor? | 50Hz | ASTMD150 | 3.4E-03 | |
| 60Hz | ASTMD150 | 3.4E-03 | ||
| 1MHz | ASTMD150 | 2.1E-03 | ||
| Surface Resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Dielectric Constant | 50Hz | ASTMD150 | 2.52 | |
| 60Hz | ASTMD150 | 2.52 | ||
| 1MHz | ASTMD150 | 2.46 | ||
| Volume Resistivity | ASTMD257 | 2.3E+16 | ohms·cm | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 15 | kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 49.7 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-1 | |
| 6.0mm | UL94 | V-0 | ||
| RadiantPanelListing(UL) | UL94 | RP100 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.