PPO NORYL™ NH7010 BK1005 SABIC INNOVATIVE SHANGHAI

Unit Price:
$4112 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Chemical resistance High rigidity
Application Areas:Electrical applications electrical equipment
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	300°C/5.0 kg	ASTM D1238	10	g/10 min
Melt Volume flow Rate	300°C/5.0 kg	ISO 1133	10.0	cm3/10min
Moisture Absorption	Saturation, 23°C	ISO 62	0.25	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.050	%
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 2	ASTM D638	2250	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2500	Mpa
Tensile Elongation	Yield 3	ASTM D638	5.2	%
	Tensile Elongation	Yield	ISO 527-2/50	4.9	%
		Tensile Elongation	Break 3	ASTM D638	41	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	8.4	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2470	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2520	Mpa
Tensile Strength	Yield 3	ASTM D638	68.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	69.0	Mpa
		Tensile Strength	Break 3	ASTM D638	49.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	63.0	Mpa
Flexural Stress	-- 5, 6	ISO 178	109	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	102	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	105	°C
RTI Imp		UL 746	105	°C
RTI Elec		UL 746	105	°C
Vicat Softening Temperature	--	ASTM D15259	160	°C
	Vicat Softening Temperature	--	ISO 306/B50	161	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	162	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	8.2E-5	cm/cm/°C
	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	8.2E-5	cm/cm/°C
	Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	8.2E-5	cm/cm/°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	139	°C

Electrical performance	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 3
Hot-wire Ignition	UL 746	PLC 0
High Voltage Arc Tracking Rate	UL 746	PLC 4
Arc Resistance	ASTM D495	PLC 6

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	30 到 70	%
Rear Temperature	265 到 315	°C
Middle Temperature	275 到 320	°C
Front Temperature	290 到 325	°C
Nozzle Temperature	300 到 325	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	20 到 100	rpm
Drying Temperature	110 到 120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	300 到 325	°C
Mold Temperature	80 到 110	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	38.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm, Testing by SABIC	UL 94	V-0
Flame Rating	Flame Rating	2.0 mm, Testing by SABIC	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.