Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.080	%
Outdoor Suitability		UL 746C	f1
Melt Mass-Flow Rate	280°C/5.0 kg	ASTM D1238	20	g/10 min
Melt Volume flow Rate	280°C/5.0 kg	ISO 1133	23.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 6, 7	ISO 178	87.0	Mpa
	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	98.0	Mpa
	Flexural Stress	Flexural Stress	Yield, 100 mm Span 5	ASTM D790	91.0	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	76.0	mg
Tensile Strength	Yield 3	ASTM D638	60.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	58.0	Mpa
		Tensile Strength	Break 3	ASTM D638	47.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	50.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2580	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2600	Mpa
Tensile Elongation	Yield 3	ASTM D638	3.6	%
	Tensile Elongation	Yield	ISO 527-2/50	3.2	%
		Tensile Elongation	Break 3	ASTM D638	9.0	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	9.2	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2500	Mpa
	Flexural Modulus	100 mm Span 5	ASTM D790	2300	Mpa
	Flexural Modulus	Flexural Modulus	-- 6	ISO 178	2350	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D15259	104	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	107	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	7.7E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	8.1E-5	cm/cm/°C
Thermal Conductivity		ASTM C177	0.24	W/m/K
RTI		UL 746	95.0	°C
RTI Imp		UL 746	80.0	°C
RTI Elec		UL 746	95.0	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	95.0	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Bf	95.0	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	78.0	°C
			Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	86.0	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	82.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	3.20 mm, in Oil	ASTM D149	19	KV/mm
Comparative Tracking Index		UL 746	PLC 1
Hot-wire Ignition		UL 746	PLC 2
High Voltage Arc Tracking Rate		UL 746	PLC 4
High Amp Arc Ignition		UL 746	PLC 2
Arc Resistance		ASTM D495	PLC 7
Dissipation Factor?	100 Hz	ASTM D150	0.013
Dissipation Factor?	Dissipation Factor?	100 kHz	ASTM D150	5.5E-3
Dielectric Constant	100 Hz	ASTM D150	2.74
Dielectric Constant	Dielectric Constant	100 kHz	ASTM D150	2.60
Volume Resistivity		ASTM D257	1.8E+16	ohms·cm

Injection	Test Result	Unit
Drying Temperature	75 到 80	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	250 到 275	°C
Mold Temperature	55 到 75	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	30 到 70	%
Rear Temperature	215 到 265	°C
Middle Temperature	225 到 270	°C
Front Temperature	240 到 275	°C
Nozzle Temperature	250 到 275	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	20 到 100	rpm
Vent Depth	0.038 到 0.051	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	50.0	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	720	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	120

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ASTM D2863	39	%
Flame Rating	1.0 mm	UL 94	HB
	Flame Rating	1.5 mm	UL 94	V-0
	Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.