PPO FLEX NORYL™ PX9406P-111 SABIC INNOVATIVE SHANGHAI
91
- Unit Price:
- $4173 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Electronic communication Electronic communication building materials Profile
- Color:--
- Grade:Injection grade
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melt Mass-Flow Rate | 250°C/10.0 kg | ASTM D1238 | 3.9 | g/10 min |
Melt Volume flow Rate | 280°C/10.0 kg | ISO 1133 | 27.0 | cm3/10min |
280°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
300°C/5.0 kg | ISO 1133 | 23.0 | cm3/10min | |
Moisture Absorption | 24 hr | ASTM D570 | 0.070 | % |
Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Stress | Yield | 内部方法 | 63.0 | Mpa |
Yield | ISO 527-2/50 | 73.0 | Mpa | |
Tensile Strain | Break | 内部方法 | 85 | % |
Break | ISO 527-2/50 | 4.5 | % | |
Flexural Modulus | -- | ASTM D790 | 2350 | Mpa |
-- 2 | ISO 178 | 2600 | Mpa | |
Flexural Strength | -- | ASTM D790 | 99.0 | Mpa |
-- 2, 3 | ISO 178 | 108 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Linear thermal expansion coefficient | Flow : -30 to 30°C | TMA | 7.0E-5 | cm/cm/°C |
Flow : -40 to 40°C | ISO 11359-2 | 6.6E-5 | cm/cm/°C | |
Across Flow : -40°C | ISO 11359-2 | 7.6E-5 | cm/cm/°C | |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 136 | °C |
1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 125 | °C | |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 5 | ISO 75-2/Af | 117 | °C | |
Ball PressureTest | 125°C | IEC 60695-10-2 | 通过 | |
Vicat Softening Temperature | -- | ISO 306/A120 | 151 | °C |
-- | ISO 306/B120 | 142 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Surface Resistivity | ASTM D257 | 1.0E+16 | ohms | |
Dielectric Constant | 60 Hz | ASTM D150 | 2.80 | |
50 kHz | ASTM D150 | 2.80 |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melt Viscosity | 280°C, 1500 sec^-1 | ISO 11443 | 278 | Pa·s |
Injection | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying Temperature | 105 到 110 | °C | ||
Suggested Max Moisture | 0.020 | % | ||
Processing (Melt) Temp | 275 到 305 | °C | ||
Mold Temperature | 70 到 100 | °C | ||
Drying Time | 3.0 到 4.0 | hr | ||
Suggested Shot Size | 30 到 70 | % | ||
Rear Temperature | 245 到 295 | °C | ||
Middle Temperature | 255 到 300 | °C | ||
Front Temperature | 265 到 305 | °C | ||
Nozzle Temperature | 275 到 305 | °C | ||
Back Pressure | 0.300 到 0.700 | Mpa | ||
Screw Speed | 20 到 100 | rpm | ||
Vent Depth | 0.038 到 0.051 | mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 9.0 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 0.40 mm | UL 94 | V-2 | |
0.75 mm | UL 94 | V-0 | ||
2.5 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.