Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24 hr | ASTM D570 | 0.20 | % |
Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break | ASTM D638 | 50 | % |
Flexural Modulus | 100 mm Span | ASTM D790 | 2300 | Mpa |
Flexural Strength | Yield, 100 mm Span | ASTM D790 | 81.0 | Mpa |
Tensile Strength | Yield | ASTM D638 | 53.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 123 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 121 | °C |
Coefficient of Linear Thermal Expansion (Flow) | 0 to 100°C | ASTM E831 | 9.4E-5 | cm/cm/°C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Time | | | 3.0 到 4.0 | hr |
Suggested Shot Size | | | 30 到 70 | % |
Rear Temperature | | | 230 到 280 | °C |
Middle Temperature | | | 245 到 290 | °C |
Front Temperature | | | 255 到 295 | °C |
Nozzle Temperature | | | 265 到 295 | °C |
Back Pressure | | | 0.300 到 0.700 | Mpa |
Screw Speed | | | 20 到 100 | rpm |
Vent Depth | | | 0.038 到 0.051 | mm |
Drying Temperature | | | 95 到 105 | °C |
Suggested Max Moisture | | | 0.020 | % |
Processing (Melt) Temp | | | 265 到 295 | °C |
Mold Temperature | | | 65 到 95 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | -30°C, Energy at Peak | ASTM D3763 | 25.0 | J |
Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 53.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.