Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Saturation, 23°C | ISO 62 | 0.23 | % |
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.060 | % |
Melt Volume flow Rate | 280°C/5.0 kg | ISO 1133 | 8.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO 527-2/50 | 55.0 | Mpa |
Tensile Stress | Break | ISO 527-2/50 | 50.0 | Mpa |
Tensile Strain | Yield | ISO 527-2/50 | 5.0 | % |
Tensile Strain | Break | ISO 527-2/50 | 30 | % |
Tensile Modulus | | ISO 527-2/1 | 2300 | Mpa |
Flexural Modulus | | ISO 178 | 2200 | Mpa |
Flexural Stress | | ISO 178 | 75.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 115 | °C |
Vicat Softening Temperature | -- | ISO 306/B50 | 135 | °C |
Vicat Softening Temperature | -- | ISO 306/B120 | 140 | °C |
Linear thermal expansion coefficient | Flow : 23 to 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow : 23 to 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 100 到 120 | °C |
Processing (Melt) Temp | | | 280 到 300 | °C |
Mold Temperature | | | 80 到 120 | °C |
Drying Time | | | 2.0 到 3.0 | hr |
Rear Temperature | | | 240 到 260 | °C |
Middle Temperature | | | 260 到 280 | °C |
Front Temperature | | | 280 到 300 | °C |
Nozzle Temperature | | | 260 到 280 | °C |
Hopper Temperature | | | 60 到 80 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO 180/1A | 5.0 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO 180/1A | 15 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.