Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.20 到 0.30 | % |
Modeling Shrinkage | Across Flow : 3.20 mm | 内部方法 | 0.65 到 0.85 | % |
Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.50 | % |
Moisture Absorption | Equilibrium, 50% RH | ASTM D570 | 1.0 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break | ASTM D638 | 7.0 | % |
Flexural Modulus | 100 mm Span | ASTM D790 | 8580 | Mpa |
Flexural Strength | Yield, 100 mm Span | ASTM D790 | 248 | Mpa |
Tensile Strength | Yield | ASTM D638 | 151 | Mpa |
Tensile Strength | Break | ASTM D638 | 158 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTM D15255 | 248 | °C |
Coefficient of Linear Thermal Expansion (Flow) | -20 to 150°C | ASTM E831 | 2.0E-5 到 3.1E-5 | cm/cm/°C |
RTI | | UL 746 | 50.0 | °C |
RTI Imp | | UL 746 | 50.0 | °C |
RTI Elec | | UL 746 | 50.0 | °C |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 254 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 240 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | | UL 746 | PLC 2 | |
High Amp Arc Ignition | | UL 746 | PLC 2 | |
Hot-wire Ignition | | UL 746 | PLC 0 | |
High Voltage Arc Tracking Rate | | UL 746 | PLC 1 | |
Arc Resistance | | ASTM D495 | PLC 6 | |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Time | | | 3.0 到 4.0 | hr |
Suggested Shot Size | | | 30 到 50 | % |
Rear Temperature | | | 265 到 305 | °C |
Middle Temperature | | | 270 到 305 | °C |
Front Temperature | | | 275 到 305 | °C |
Nozzle Temperature | | | 280 到 305 | °C |
Back Pressure | | | 0.300 到 1.40 | Mpa |
Screw Speed | | | 20 到 100 | rpm |
Vent Depth | | | 0.013 到 0.038 | mm |
Drying Temperature | | | 95 到 105 | °C |
Suggested Max Moisture | | | 0.070 | % |
Processing (Melt) Temp | | | 280 到 305 | °C |
Mold Temperature | | | 75 到 120 | °C |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTM D785 | 120 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.5 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.