Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.30to0.50 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.070 | % |
Moisture Absorption | Equilibrium,23°C | ASTMD570 | 0.22 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Break | ASTMD638 | 74.5 | Mpa |
Tensile Elongation | Break | ASTMD638 | 5.0 | % |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 4000 | Mpa |
Flexural Strength | Break,50.0mmSpan | ASTMD790 | 120 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTMD15254 | 148 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C |
RTIElec | | UL746 | 110 | °C |
Evolution Calendar intelligent importer | | UL746 | 105 | °C |
RTIStr | | UL746 | 110 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 50Hz | ASTMD150 | 1.7E-03 | |
Dissipation Factor? | 60Hz | ASTMD150 | 1.7E-03 | |
Dissipation Factor? | 1MHz | ASTMD150 | 1.6E-03 | |
Comparative Tracking Index | CTI | UL746 | PLC2 | |
Dielectric Constant | 50Hz | ASTMD150 | 3.00 | |
Dielectric Constant | 60Hz | ASTMD150 | 3.00 | |
Dielectric Constant | 1MHz | ASTMD150 | 3.00 | |
Volume Resistivity | | ASTMD257 | 1E+15 | ohms·cm |
Hot-wire Ignition | HWI | UL746 | PLC1 | |
High Amp Arc Ignition | HAI | UL746 | PLC2 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | L-Sale | ASTMD785 | 104 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ASTMD2863 | 34 | % |
UL flame retardant rating | 1.5mm | UL94 | V-1 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.