PPO NORYL™ PX1112-701 SABIC INNOVATIVE US
69
- Unit Price:
- $4050 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Low Specific Gravity
- Application Areas:Automotive body panels Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.060 | % | |
| Melt Volume flow Rate | 280°C/5.0 kg | ISO 1133 | 6.00 | cm3/10min |
| Modeling Shrinkage - Flow | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO 178 | 70.0 | Mpa | |
| Tensile Stress | Yield | ISO 527-2/50 | 40.0 | Mpa |
| Break | ISO 527-2/50 | 40.0 | Mpa | |
| Tensile Strain | Yield | ISO 527-2/50 | 3.0 | % |
| Break | ISO 527-2/50 | 30 | % | |
| Tensile Modulus | ISO 527-2/1 | 2100 | Mpa | |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 Wheel | 内部方法 | 65.0 | mg |
| Flexural Modulus | ISO 178 | 1900 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | Flow : 23 to 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Across Flow : 23 to 80°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
| Heat Deflection Temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 120 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 105 | °C | |
| Vicat Softening Temperature | -- | ISO 306/A50 | 130 | °C |
| -- | ISO 306/B50 | 120 | °C | |
| -- | ISO 306/B120 | 125 | °C | |
| Thermal Conductivity | ISO 8302 | 0.23 | W/m/K | |
| Ball PressureTest | 73 to 77°C | IEC 60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume Resistivity | IEC 60093 | 1.0E+15 | ohms·cm | |
| Relative Permittivity | 50 Hz | IEC 60250 | 2.70 | |
| 60 Hz | IEC 60250 | 2.70 | ||
| 1 MHz | IEC 60250 | 2.60 | ||
| Dissipation Factor? | 50 Hz | IEC 60250 | 4.0E-4 | |
| 60 Hz | IEC 60250 | 4.0E-4 | ||
| 1 MHz | IEC 60250 | 1.0E-3 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 2.0 到 3.0 | hr | ||
| Rear Temperature | 240 到 260 | °C | ||
| Middle Temperature | 260 到 280 | °C | ||
| Front Temperature | 280 到 300 | °C | ||
| Nozzle Temperature | 260 到 280 | °C | ||
| Hopper Temperature | 60 到 80 | °C | ||
| Drying Temperature | 100 到 120 | °C | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Mold Temperature | 80 到 120 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 17 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 17 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 80.0 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.6 mm, Testing by SABIC | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.