PPO NORYL™ GFN3-701 SABIC INNOVATIVE NANSHA

153

Unit Price:
$3843 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:enhance Glass fiber reinforced Hydrolysis resistance
Application Areas:Lawn equipment Electrical field Electrical appliances Electronic field Electronic display Engine hood parts Non specific food Nursing supplies Architectural application Automotive External Parts Outdoor applications Liquid handling Medical supplies Garden equipment Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.20mm	内部方法	0.10to0.40	%
Moisture Absorption	24hr	ASTMD570	0.060	%
Melt Mass-Flow Rate	300°C/5.0kg	ASTMD1238	8.7	g/10min
Melt Volume flow Rate	300°C/5.0kg	ISO1133	7.82	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break	ISO527-2	117	Mpa
Tensile Strain	Break	ISO527-2	1.8	%
Tensile Modulus		ISO527-2/1	8740	Mpa
Flexural Modulus	100mmSpan4	ASTMD790	7170	Mpa
	Flexural Modulus	50.0mmSpan5	ASTMD790	8000	Mpa
	Flexural Modulus	Flexural Modulus		ISO178	8710	Mpa
Flexural Strength	Yield,50.0mmSpan5	ASTMD790	180	Mpa
Flexural Strength	Flexural Strength	Yield,100mmSpan4	ASTMD790	162	Mpa
Flexural Stress		ISO178	183	Mpa
Tensile Modulus		ASTMD638	9150	Mpa
Tensile Strength	Break	ASTMD638	116	Mpa
Tensile Elongation	Break	ASTMD638	2.0	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	137	°C
Heat Deflection Temperature	Heat Deflection Temperature	0.45MPa,Unannealed,64.0mmSpan	ISO75-2/Bf	143	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	142	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed,6.40mm	ASTMD648	158	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	137	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,6.40mm	ASTMD648	138	°C
RTIElec		UL746	90.0	°C
Evolution Calendar intelligent importer		UL746	90.0	°C
RTIStr		UL746	90.0	°C
Vicat Softening Temperature	--	ISO306/B50	143	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	147	°C
Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	3.1E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	6.2E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	CTI	UL746	PLC4
High Amp Arc Ignition	HAI	UL746	PLC4
High Voltage Arc Tracking Rate	HVTR	UL746	PLC3
Dissipation Factor?	50Hz	ASTMD150	9E-04
Dissipation Factor?	Dissipation Factor?	60Hz	ASTMD150	9E-04
Dielectric Constant	50Hz	ASTMD150	2.93
Dielectric Constant	Dielectric Constant	60Hz	ASTMD150	2.93
Hot-wire Ignition	HWI	UL746	PLC4
Dielectric Strength	3.20mm,inOil	ASTMD149	22	KV/mm
Arc Resistance		ASTMD495	PLC7

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	-30°C	ISO180/1A	12	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	12	kJ/m²
Unnotched Izod Impact Strength	-30°C	ISO180/1U	36	kJ/m²
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO180/1U	32	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	47	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	39	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	L-Sale	ASTMD785	108

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB
Oxygen Index		ASTMD2863	26	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.