Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.10to0.30 | % |
Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.20to0.40 | % |
Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 13 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ASTMD638 | 6260 | Mpa |
Tensile Strength | Yield | ASTMD638 | 109 | Mpa |
Tensile Strength | Break | ASTMD638 | 109 | Mpa |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 5720 | Mpa |
Tensile Elongation | Break | ASTMD638 | 2.4 | % |
Flexural Strength | Break,50.0mmSpan | ASTMD790 | 170 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 164 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 159 | °C |
Vicat Softening Temperature | | ASTMD15255 | 175 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1.60mm,inOil | ASTMD149 | 34 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 16.5 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.