PPO NORYL™ GFN1-701S SABIC INNOVATIVE SHANGHAI
104
- Unit Price:
- $3927 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Flame retardant Glass fiber reinforced High temperature resistan
- Application Areas:household electrical appl Automotive interior parts Water sports equipment
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.50 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.060 | % |
| Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 17 | g/10min |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 16.4 | cm3/10min |
| Outdoor Suitability | UL746C | f1 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ASTMD638 | 4350 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 63.0 | Mpa |
| Tensile Stress | Break | ISO527-2 | 64.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.0 | % |
| Tensile Modulus | ISO527-2/1 | 4400 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | 3.0 | % |
| Flexural Modulus | 50.0mmSpan4 | ASTMD790 | 3840 | Mpa |
| 100mmSpan5 | ASTMD790 | 3590 | Mpa | |
| ISO178 | 4160 | Mpa | ||
| Flexural Strength | Yield,50.0mmSpan4 | ASTMD790 | 116 | Mpa |
| Yield,100mmSpan5 | ASTMD790 | 108 | Mpa | |
| Flexural Stress | ISO178 | 122 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 124 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 132 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 131 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 122 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 125 | °C | |
| RTIElec | UL746 | 90.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 131 | °C |
| -- | ISO306/B120 | 134 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 5.1E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot-wire Ignition | HWI | UL746 | PLC5 | |
| High Amp Arc Ignition | HAI | UL746 | PLC4 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 | |
| Dissipation Factor? | 1MHz | ASTMD150 | 1.4E-03 | |
| Dielectric Constant | 1MHz | ASTMD150 | 2.90 | |
| Arc Resistance | ASTMD495 | PLC7 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 9.4 | kJ/m² |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 25 | kJ/m² |
| 23°C | ISO180/1U | 28 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 33 | kJ/m² |
| 23°C | ISO179/1eU | 35 | kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 21.7 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | L-Sale | ASTMD785 | 104 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.