PA66 Zytel® 70G35HSLRA4 BK267 DUPONT USA
102
- Unit Price:
- $3620 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability wear resistant
- Application Areas:Electronic appliances Home appliance components Connector
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.40 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 5.5 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.7 | % | |
| MediumDensity | 1.27 | g/cm³ | ||
| Ejection Temperature | 210 | °C | ||
| SpecificHeatCapacityofMelt | 2300 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.22 | W/m/K | ||
| Melt Volume flow Rate | 275°C/5.0kg | ISO1133 | 40.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO178 | 300 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 210 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.0 | % |
| Tensile Modulus | ISO527-2 | 11000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 255 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 250 | °C | |
| Linear thermal expansion coefficient | MD：55to160°C | ISO11359-2 | 1.4E-05 | cm/cm/°C |
| TD：-- | ISO11359-2 | 6.9E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 6.2E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.4E-04 | cm/cm/°C | |
| MD：-- | ISO11359-2 | 2.2E-05 | cm/cm/°C | |
| MD：-40to23°C | ISO11359-2 | 2.3E-05 | cm/cm/°C | |
| Melting Temperature | ISO11357-3 | 260 | °C | |
| Glass Transition Temperature | ISO11357-2 | 80.0 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 255 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | IEC60112 | 450 | V | |
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 80 | kJ/m² |
| 23°C | ISO179/1eU | 80 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 6.00 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.70mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.70mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS Flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 5E-04 | g |
| Burning Rate | 1.00mm | ISO3795 | 18 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.