PBT/PC VALOX™ V3900WX-BK1H078 SABIC INNOVATIVE SHANGHAI
161
- Unit Price:
- $4603 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact Low warpage Dimensional stability High toughness Weather resistance
- Application Areas:Charging station Wire and cable Electronic and electrical Automotive sector Communication equipment Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.70to1.0 | % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.10 | % |
| 平衡,23°C,50%RH | ISO62 | 0.030 | % | |
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 11 | g/10min |
| Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 9.00 | cm3/10min |
| Density | ISO1183 | 1.30 | g/cm³ | |
| ASTMD792 | 1.30 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | 屈服 | 内部方法 | 48.0 | Mpa |
| 屈服 | ASTMD638 | 53.0 | Mpa | |
| 断裂 | ASTMD638 | 43.0 | Mpa | |
| Tensile Stress | 断裂 | ISO527-2/50 | 40.0 | Mpa |
| 屈服 | ISO527-2/50 | 51.0 | Mpa | |
| Tensile Strain | 断裂 | ISO527-2/50 | 42 | % |
| 屈服 | ISO527-2/50 | 4.0 | % | |
| Tensile Modulus | ASTMD638 | 2200 | Mpa | |
| ISO527-2/1 | 2100 | Mpa | ||
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 | % |
| 断裂 | 内部方法 | 250 | % | |
| 断裂3 | ASTMD638 | 50 | % | |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2200 | Mpa |
| ISO178 | 2130 | Mpa | ||
| Flexural Strength | ISO178 | 73.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 80.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火,6.40mm | ASTMD648 | 119 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 75.0 | °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 96.0 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 77.0 | °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 8.8E-05 | cm/cm/°C |
| TD：-40到40°C | ASTME831 | 9E-05 | cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 8.8E-05 | cm/cm/°C | |
| RTI Str | UL746 | 120 | °C | |
| RTI Imp | UL746 | 120 | °C | |
| RTI Elec | UL746 | 120 | °C | |
| Vicat Softening Temperature | ASTMD152510 | 105 | °C | |
| -- | ISO306/B50 | 122 | °C | |
| -- | ISO306/B120 | 124 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | ASTMD257 | 6E+16 | ohms |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | -40°C,TotalEnergy | ASTMD3763 | 50.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 50.0 | J | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 52 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 110 | J/m |
| 23°C | ASTMD256 | 800 | J/m | |
| -30°C | ISO180/1A | 8.4 | kJ/m² | |
| 23°C | ISO180/1A | 41 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 | °C |
| 3.0mm11 | IEC60695-2-12 | 960 | °C | |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| 3.0mm | IEC60695-2-13 | 725 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.