PBT/PC VALOX™ 357U-BK1066 SABIC INNOVATIVE SHANGHAI
242
- Unit Price:
- $3714 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance
- Application Areas:Roller switch Shell
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD3 | 内部方法 | 1.0到1.4 | % |
| MD4 | 内部方法 | 0.80到1.1 | % | |
| TD3 | 内部方法 | 1.2到1.6 | % | |
| TD4 | 内部方法 | 0.90到1.3 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.080 | % |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 8.00 | cm3/10min |
| Specific volume | ASTMD792 | 0.750 | cm³/g | |
| Outdoor applicability | UL746C | f2 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength 6 | Yield,50.0mmSpan | ASTMD790 | 82.7 | Mpa |
| Break,50.0mmSpan | ASTMD790 | 82.7 | Mpa | |
| Tensile strength 5 | Yield | ASTMD638 | 48.3 | Mpa |
| Break | ASTMD638 | 48.3 | Mpa | |
| Elongation rate 5 | Break | ASTMD638 | 110 | % |
| Bending modulus 6 | 50.0mmSpan | ASTMD790 | 2070 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | UL746 | 140 | °C | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 98.9 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 9.2E-05 | cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.2E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 19 | KV/mm |
| 1.60mm,inOil | ASTMD149 | 25 | KV/mm | |
| 3.20mm,inAir | ASTMD149 | 19 | KV/mm | |
| Dielectric constant | 100Hz | ASTMD150 | 3.20 | |
| 1MHz | ASTMD150 | 3.20 | ||
| Volume resistivity | ASTMD257 | >1.2E+16 | ohms·cm | |
| Dissipation factor | 100Hz | ASTMD150 | 3E-03 | |
| 1MHz | ASTMD150 | 0.030 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Hot wire ignition | HWI | UL746 | PLC2 | |
| Arc resistance 8 | ASTMD495 | PLC6 | ||
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Falling hammer impact | 23°C7 | ASTMD3029 | 43.4 | J |
| 23°C | ASTMD3029 | 43.4 | J | |
| Cantilever beam without notch impact strength | 23°C | ASTMD4812 | 3200 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 117 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTMD2863 | 30 | % | |
| UL flame retardant rating | 0.46mm | UL94 | HB | |
| 0.64mm | UL94 | V-0 | ||
| 3.0mm | UL94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.